GÄNGIGE VENTILGUSSWERKSTOFFE METALLURGIE
| Gusslegierung | Ähnliche Schmiedeeisenbezeichnung | Spezifikation | UNS-Nr. | C | Cr | Ni | Mo | Cu | Fe | Cb | Andere | Zugfestigkeit (ksi) | Ertrag (ksi) | Elong |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| CA6NM | 415, F6NM | ASTM-A743, A487 | J91540 | 0.06 | 11.5-14.0 | 3.5-4.5 | .4-1.0 | – | BAL | – | – | 110 | 80 | 17% |
| CA15 | 410 | ASTM-A217, A743 | J91150 | 0.15 | 11.5-14.0 | 1 | 0.5 | 0.5 | BAL | – | – | 90 | 65 | 18% |
| CB7Cu-1 | 17-4 PH | ASTM-A747, AMS-5398C | J92180 | 0.06 | 15.5-17.7 | 3.6-4.6 | – | 2.5-3.2 | BAL | .15-.35 | – | 135 H1100 Zustand | 100 | 9% |
| CF3 | 304L | ASTM-A351, A743, A744 | J92500 | 0.03 | 17.0-21.0 | 8.0-12.0 | 0.5 | – | BAL | – | – | 70 | 30 | 35% |
| CF3MN | 316LN | ASTM-A743, A351 | J92804 | 0.03 | 17.0-21.0 | 9.0-13.0 | 2.0-3.0 | – | BAL | – | N- 0,10-0,20 | 75 | 37 | 35% |
| CF3M | 316L | ASTM-A351, A743, A744 | J92800 | 0.03 | 17.0-21.0 | 9.0-13.0 | 2.0-3.0 | – | BAL | – | – | 70 | 30 | 30% |
| CF8 | 304 | ASTM-A351, A743, A744 | J92600 | 0.08 | 18.0-21.0 | 8.0-11.0 | 0.5 | – | BAL | – | – | 70 | 30 | 35% |
| CF8C | 347 | ASTM-A351, A743, A744 | J92710 | 0.08 | 18.0-21.0 | 9.0-12.0 | 0.5 | – | BAL | 8xC-1.0 | – | 70 | 30 | 30% |
| CF8M | 316 | ASTM-A351, A743, A744 | J92900 | 0.08 | 18.0-21.0 | 9.0-12.0 | 2.0-3.0 | – | BAL | – | – | 70 | 30 | 30% |
| CG3M | 317L | ASTM-A351, A743, A744 | J92999 | 0.03 | 18.0-21.0 | 9.0-13.0 | 3.0-4.0 | – | BAL | – | – | 75 | 35 | 25% |
| CG8M | 317 | ASTM-A351, A743, A744 | J93000 | 0.08 | 18.0-21.0 | 9.0-13.0 | 3.0-4.0 | – | BAL | – | – | 75 | 35 | 25% |
| CN7M | Legierung 20 | ASTM-A351, A743, A744 | N08007 | 0.07 | 19.0-22.0 | 27.5-30.5 | 2.0-3.0 | 3.0-4.0 | BAL | – | – | 62 | 25 | 35% |
| CN2MCuN | 904L | N08904 | 0.02 | 19.0-23.0 | 23.0-28.0 | 4.0-5.0 | 1.0-2.0 | BAL | – | – | 65 | 28 | 35% | |
| CK3MCuN | Avesta 254-SMO | ASTM-A351, A743, A744 | J93254 | 0.025 | 19.5-20.5 | 17.5-19.5 | 6.00-7.00 | 0.50-1.00 | BAL | – | N 0,18-0,24 | 80 | 38 | 35% |
| CN3MN | AL6XN | ASTM-A351, A743, A744 | J94651 | 0.030 | 20.0-22.0 | 23.5-25.5 | 6.0-7.0 | 0.75 | BAL | – | N 0,18-1,26 | 80 | 38 | 35% |
| CX2MW | Hastelloy C-22 | ASTM A494 | N26022 | 0.02 | 20.0-22.5 | BAL | 12.5-14.5 | – | 2.0-6.0 | – | W-2,5-3,5 | 80 | 45 | 30% |
| CW2M | Hastelloy C4C | ASTM-A494, A990 | N26455 | 0.02 | 15.0-17.5 | BAL | 15.0-17.5 | – | 2 | – | – | 72 | 40 | 20% |
| CW6M | Hastelloy C modifiziert | ASTM-A494 | N30107 | 0.07 | 17.0-20.0 | BAL | 17.0-20.0 | – | 3 | – | – | 72 | 40 | 25% |
| CW6MC | Inconel 625 | ASTM-A494, MIL-C-24615 | N26625 | 0.06 | 20.0-23.0 | BAL | 8.0-10.0 | – | 5 | 3.15-4.5 | – | 70 | 40 | 25% |
| CW12MW | Hastelloy C | ASTM-A494 | N30002 | 0.12 | 15.5-17.5 | BAL | 16.0-18.0 | – | 4.5-7.5 | – | W-3,75-5,25, V-,20-,40 | 72 | 40 | 4% |
| CW12MW | Hastelloy C-276 | ASTM-A494 | N30002 | 0.02 | 15.5-17.5 | BAL | 16.0-18.0 | – | 4.5-7.5 | – | W-3,75-5,25, V-,20-,40 | 72 | 40 | 4% |
| CY40 | Inconel 600 | ASTM-A494 | N06040 | 0.4 | 14.0-17.0 | BAL | – | – | 11 | – | – | 70 | 28 | 30% |
| CZ100 | Nickelguss | ASTM-A494 | N02100 | 1 | – | 95,0 Min. | – | 1.25 | 3 | – | – | 50 | 18 | 10% |
| N7M | Hastelloy B modifiziert | ASTM-A494 | N30007 | 0.07 | 1 | BAL | 30.0-33.0 | – | 3 | – | – | 76 | 40 | 20% |
| N12MV | Hastelloy B | ASTM-A494 | N30012 | 0.12 | 1 | BAL | 26.0-30.0 | – | 4.0-6.0 | – | – | 76 | 40 | 6% |
| M35-1 | Monel 400 | ASTM-A494, A990 | N24135 | 0.35 | – | BAL | – | 26.0-33.0 | 3.5 | 0.5 | Si 1,25 | 65 | 25 | 25% |
| M35-2 | Monel | ASTM-A494 | N04020 | 0.35 | – | BAL | – | 26.0-33.0 | 3.5 | – | Si 2.0 | 65 | 30 | 25% |
| M35-B / M30H | H-Monel | ASTM-A494, QQ-N-288 Komp. B | N24030 | 0.3 | – | BAL | – | 27.0-33.0 | 2.5 | – | Si 2,7-3,9 | 700 | 60 | 10% |
| M35-C | Monel | QQ-N-288 Komp. C | N24025 | 0.2 | – | BAL | – | 27.0-31.0 | 2.5 | – | Si 3,3-3,7 | 120 | 80 | 10% |
| M35-D / M25S | S-Monel | ASTM A494, QQ-N-288 Komp. D | N24025 | 0.25 | – | BAL | – | 27.0-31.0 | 2.5 | – | Si 3,5-4,5 | – | – | – |
| M30C / M35W | Schweißbares Monel | ASTM-A494, QQ-N-288 Komp. E | N24130 | 0.3 | – | BAL | – | 26.0-33.0 | 3.5 | – | Si 1,0-2,0, Cb 1,0-3,0 | 65 | 32.5 | 25% |
| 952 | Al Bronze Klasse A | ASTM-B148 | C95200 | – | – | – | – | 86,0 Minuten | 2.5-4.0 | – | Al 8,5-9,5 | 65 | 25 | 20% |
| 954 | Aluminium-Bronze | ASTM-B148 | C95400 | – | – | 1,5 max | – | 83,0 Minuten | 3.0-5.0 | – | Al 10,0-11,5 | 75 | 30 | 12% |
| 955 | Aluminium-Bronze | ASTM-B148 | C95500 | – | – | 3.0-5.5 | – | 78,0 Minuten | 3.0-5.0 | – | Al 10,0-11,5 | 90 | 40 | 6% |
| 958 | Ni-Al-Brz | ASTM-B148 | C95800 | – | – | 4.0-5.0 | – | 79,0 Min. | 3.0-4.5 | – | Al 8,5-9,5 Pb 0,03 max | 85 | 35 | 15% |
| 964 | 70*30 Kupfer-Nickel | ASTM-B369 | C96400 | 0.15 | – | 28.0-32.0 | – | BAL | .25-1.5 | 0.5-1.5 | Mn 1,5 | 60 | 32 | 20% |
| CD4MCuN | Duplex Klasse 1B | ASTM-A890, A995 | J93372 | 0.04 | 24.5-26.5 | 4.75-6.0 | 1.75-2.25 | 2.75-3.25 | BAL | – | N 0,10-0,25 | 100 | 70 | 16% |
| CD3MCuN | Duplex Klasse 1C | ASTM-A890 | J93373 | 0.03 | 24-26.7 | 5.6-6.7 | 2.9-3.8 | 1.4-1.9 | BAL | – | N 0,22-0,33 | 100 | 65 | 25% |
| CE8MN | Duplex Klasse 2A | ASTM-A351, A890, A995 | J93345 | 0.08 | 22.5-25.5 | 8.0-11.0 | 3.00-4.50 | – | BAL | – | N 0,10-0,30 | 95 | 65 | 25% |
| CD6MN | Duplex Klasse 3A | ASTM-A890, A995 | J93371 | 0.06 | 24.0-27.0 | 4.0-6.0 | 1.75-2.50 | – | BAL | – | N 0,10-0,25 | 95 | 65 | 25% |
| CD3MN | Duplex Klasse 4A | ASTM-A890, A995 | J92205 | 0.03 | 21.0-23.5 | 4.5-6.5 | 2.5-3.5 | 1,00 max | BAL | – | N 0,10-0,30 | 90 | 60 | 25% |
| CE3MN | Duplex Klasse 5A | ASTM-A890, A995 | J93404 | 0.03 | 24.0-26.0 | 6.0-8.0 | 4.0-5.0 | – | BAL | – | N 0,10-0,03 | 100 | 75 | 18% |
| CD3MWCuN | Klasse 6A Zeron100 | ASTM-A890, A995 | J93380 | 0.03 | 24.0-26.0 | 6.5-8.5 | 3.0-4.0 | 0.5-1.0 | BAL | – | N 0,02-0,03 W 0,5-1,0 | 100 | 65 | 25% |
| HH | ASTM-A297 | ASTM-A297 | J93503 | 0.20-0.50 | 24.0-28.0 | 11.0-14.0 | 0.5 | 1 | BAL | – | – | 75 | 35 | 10% |
| HK | ASTM-A297 | ASTM-A297 | J94224 | 0.20-0.60 | 24.0-28.0 | 18.0-22.0 | 0.5 | 1 | BAL | – | – | 65 | 35 | 10% |
| HN | HI-35 | ASTM-A297 | J94213 | 0.20-0.50 | 19.0-23.0 | 23.0-27.0 | 0.5 | 1 | BAL | – | – | 63 | – | 8% |
| HT | 330 (15-35) | ASTM-A297 | N08605 | 0.35-0.75 | 15.0-19.0 | 33.0-37.0 | 0.5 | 1 | BAL | – | – | 65 | – | 4% |
| HU | (19-39) | ASTM-A297 | N08004 | 0.35-0.75 | 17.0-21.0 | 37.0-41.0 | 0.5 | 1 | BAL | – | – | 65 | – | 4% |
| HX | ACI HX | ASTM-A297 | N06006 | 0.35-0.75 | 15.0-19.0 | 64.0-68.0 | 0.5 | 1 | BAL | – | – | 60 | – | – |
| WCA | Kohlenstoffstahl | ASTM-A216 | J02502 | 0.25 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 60-85 | 30 | 24% |
| WCB | Kohlenstoffstahl | ASTM-A216 | J03002 | 0.3 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 70-95 | 36 | 22% |
| ÖRK | Kohlenstoffstahl | ASTM-A216 | J02503 | 0.25 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 70-95 | 40 | 22% |
| LCB | Kohlenstoffstahl | ASTM-A352 | J03003 | 0.3 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 65 | 35 | 24% |
| LCC | Kohlenstoffstahl | ASTM-A352 | J02505 | 0.25 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 70 | 40 | 22% |
| LC2 | ASTM-A352 | J22500 | 0.25 | – | 2.00-3.00 | 0.45-0.65 | – | BAL | – | – | 70.0-95.0 | 40.0 | 24% | |
| LC3 | ASTM-A352 | J31550 | 0.15 | – | 3.00-4.00 | – | – | BAL | – | – | 70.0-95.0 | 40.0 | 24% | |
| WC6 | ASTM-A217 | J12072 | 0.05-0.20 | 1.00-1.50 | – | 0.45-0.65 | 0.50 | BAL | – | – | 70-95 | 40 | 20% | |
| WC9 | ASTM-A217 | J21890 | 0.05-0.18 | 2.00-2.75 | – | 0.90-1.20 | 0.50 | BAL | – | – | 70-95 | 40 | 20% | |
| C5 | ASTM-A217 | J42045 | 0.20 | 4.00-6.50 | – | 0.45-0.65 | 0.50 | BAL | – | – | 90-115 | 60 | 18% | |
| 12. Jahrhundert | ASTM-A217 | J82090 | 0.20 | 8.00-10.00 | – | 0.90-1.20 | 0.50 | BAL | – | – | 90-115 | 60 | 18% | |
| C12A | Klasse 91 | ASTM-A217 | J84090 | 0.08-0.12 | 8.0-9.5 | 0.40 | 0.85-1.05 | – | BAL | 0.060-0.10 | N 0,030-0,070, V 0,18-0,25 | 85-110 | 60 | 18% |
| SC8625 | ASTM A487, A148 | 0.30 | 0.40-0.80 | 0.40-0.80 | 0.15-0.30 | 0.50 | BAL | – | – | 105-130 | 85 | 17% |
Hastelloy C276 (ASTM A 494, Klasse CW12MW)
Die Hochleistungsventile Hastelloy C276 von Instrumentation sind überragend beständig gegen verschiedene Säuren. So sind die Kugelhähne aus Hastelloy C276 beispielsweise beständig gegen Säuren wie Schwefelsäure, Salzsäure, Flusssäure, Salpetersäure und Chromsäure. Der Kugelhahn aus Hastelloy weist sogar eine gute lokale Korrosionsbeständigkeit auf.
CW12MW ist die alte originale Hastelloy C-Gusslegierung. Aufgrund ihres höheren Kohlenstoffgehalts von maximal 0,12% sowie ihrer höheren Eisen- und Wolframwerte ist diese Legierung allen anderen Legierungen in Bezug auf Korrosionsbeständigkeit und Duktilität unterlegen. CW12MW ist nicht das Gussäquivalent zu UNS N10276.
CW6M
CW6M ist die nächste entwickelte Ni-Cr-Mo-Gusslegierung. Sie wurde 1949 eingeführt, daher hat diese Legierung eine lange, erfolgreiche Geschichte. Obwohl sie einen höheren zulässigen Kohlenstoff- und Siliziumgrenzwert hat als die neueren unten aufgeführten C-Typen, wird sie normalerweise mit viel niedrigeren Kohlenstoff- und Siliziumwerten hergestellt, was ihr eine gute Korrosionsbeständigkeit gegenüber oxidierenden und reduzierenden Säuren verleiht.
CW2M
CW2M ist das Gussäquivalent von UNS N06455 und wurde 1976 entwickelt, um bei hohen Temperaturen eine bessere metallurgische Stabilität als UNS N10276 zu bieten. Ein zusätzlicher Vorteil war, dass es eine bessere Gussqualität als CW12MW ist. Seine verbesserte Leistung gegenüber CW12MW war das Ergebnis reduzierter Mengen intermetallischer Phasen in seiner Mikrostruktur. Dies wurde durch die Senkung der Kohlenstoff-, Silizium-, Eisen-, Chrom- und Molybdänwerte und den Verzicht auf Wolframzusatz erreicht.
CX2MW
CX2MW ist das gegossene Äquivalent von UNS N06022. Diese Legierung hat einen höheren Chromgehalt, aber einen niedrigeren Molybdängehalt als die anderen Hastelloy C-Typ-Legierungen. Der höhere Chromgehalt verleiht dieser Legierung eine bessere Korrosionsbeständigkeit gegenüber heißen, oxidierenden Umgebungen wie Bleichmitteln und chlorierten Salzlaugen. Der niedrigere Molybdängehalt geht jedoch zu Lasten der Beständigkeit gegenüber reduzierenden Bedingungen, in denen diese Legierungen ebenfalls häufig verwendet werden, z. B. Schwefel- und Salzsäure.
CX2M
CX2M ist das Gussäquivalent zu UNS N06059. Es enthält etwas mehr Chrom und Molybdän als CX2MW. Der höhere Chromgehalt bietet eine gute Beständigkeit gegen starke Oxidationsprozesse und der höhere Molybdängehalt eine gute Beständigkeit gegen Schwefel- und Salzsäure.
UNS N06200
UNS N06200 (Hastelloy C-2000) ist die neueste C-Typ-Legierung, ist aber nur als geschmiedetes Bauteil erhältlich, da es sich aufgrund seines extrem niedrigen Kohlenstoff- und Siliziumgehalts nicht für die Herstellung einer Gusslegierung eignet. UNS N06200 hat einen ähnlichen Chromgehalt wie UNS N06022, enthält aber mehr Molybdän und eine kleine Menge Kupfer. Der höhere Molybdängehalt zusammen mit dem Kupfer verleiht der Legierung eine bessere Beständigkeit gegen reduzierende Säuren wie Schwefel- und Salzsäure.
Verwandte Tags:
Zehn Artikel davor und danach
German 
English 
Spanish 
French 
Russian 
Portuguese 
Turkish