METALURGIA DE MATERIALES DE FUNDICIÓN DE VÁLVULAS COMUNES
| Aleación fundida | Designación forjada similar | Especificación | UNS No. | C | cr | Ni | Mes | Cu | fe | cb | Otro | Tracción (ksi) | Rendimiento (ksi) | elong |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| CA6NM | 415, F6NM | ASTM-A743, A487 | J91540 | 0.06 | 11.5-14.0 | 3.5-4.5 | .4-1.0 | – | balon | – | – | 110 | 80 | 17% |
| CA15 | 410 | ASTM-A217, A743 | J91150 | 0.15 | 11.5-14.0 | 1 | 0.5 | 0.5 | balon | – | – | 90 | 65 | 18% |
| CB7Cu-1 | 17-4PH | ASTM-A747, AMS-5398C | J92180 | 0.06 | 15.5-17.7 | 3.6-4.6 | – | 2.5-3.2 | balon | .15-.35 | – | 135 H1100 Condición | 100 | 9% |
| CF3 | 304L | ASTM-A351, A743, A744 | J92500 | 0.03 | 17.0-21.0 | 8.0-12.0 | 0.5 | – | balon | – | – | 70 | 30 | 35% |
| CF3MN | 316LN | ASTM-A743, A351 | J92804 | 0.03 | 17.0-21.0 | 9.0-13.0 | 2.0-3.0 | – | balon | – | N-0,10-0,20 | 75 | 37 | 35% |
| CF3M | 316L | ASTM-A351, A743, A744 | J92800 | 0.03 | 17.0-21.0 | 9.0-13.0 | 2.0-3.0 | – | balon | – | – | 70 | 30 | 30% |
| CF8 | 304 | ASTM-A351, A743, A744 | J92600 | 0.08 | 18.0-21.0 | 8.0-11.0 | 0.5 | – | balon | – | – | 70 | 30 | 35% |
| CF8C | 347 | ASTM-A351, A743, A744 | J92710 | 0.08 | 18.0-21.0 | 9.0-12.0 | 0.5 | – | balon | 8xC-1.0 | – | 70 | 30 | 30% |
| CF8M | 316 | ASTM-A351, A743, A744 | J92900 | 0.08 | 18.0-21.0 | 9.0-12.0 | 2.0-3.0 | – | balon | – | – | 70 | 30 | 30% |
| CG3M | 317L | ASTM-A351, A743, A744 | J92999 | 0.03 | 18.0-21.0 | 9.0-13.0 | 3.0-4.0 | – | balon | – | – | 75 | 35 | 25% |
| CG8M | 317 | ASTM-A351, A743, A744 | J93000 | 0.08 | 18.0-21.0 | 9.0-13.0 | 3.0-4.0 | – | balon | – | – | 75 | 35 | 25% |
| CN7M | Aleación 20 | ASTM-A351, A743, A744 | N08007 | 0.07 | 19.0-22.0 | 27.5-30.5 | 2.0-3.0 | 3.0-4.0 | balon | – | – | 62 | 25 | 35% |
| CN2MCuN | 904L | N08904 | 0.02 | 19.0-23.0 | 23.0-28.0 | 4.0-5.0 | 1.0-2.0 | balon | – | – | 65 | 28 | 35% | |
| CK3MCuN | Avesta 254-SMO | ASTM-A351, A743, A744 | J93254 | 0.025 | 19.5-20.5 | 17.5-19.5 | 6.00-7.00 | 0.50-1.00 | balon | – | 0,18-0,24 | 80 | 38 | 35% |
| CN3MN | AL6XN | ASTM-A351, A743, A744 | J94651 | 0.030 | 20.0-22.0 | 23.5-25.5 | 6.0-7.0 | 0.75 | balon | – | 0,18-1,26 | 80 | 38 | 35% |
| CX2MW | Hastelloy C-22 | ASTM A494 | N26022 | 0.02 | 20.0-22.5 | balon | 12.5-14.5 | – | 2.0-6.0 | – | W-2.5-3.5 | 80 | 45 | 30% |
| CW2M | Hastelloy C4C | ASTM-A494, A990 | N26455 | 0.02 | 15.0-17.5 | balon | 15.0-17.5 | – | 2 | – | – | 72 | 40 | 20% |
| CW6M | Hastelloy C Modificado | ASTM-A494 | N30107 | 0.07 | 17.0-20.0 | balon | 17.0-20.0 | – | 3 | – | – | 72 | 40 | 25% |
| CW6MC | Inconel 625 | ASTM-A494, MIL-C-24615 | N26625 | 0.06 | 20.0-23.0 | balon | 8.0-10.0 | – | 5 | 3.15-4.5 | – | 70 | 40 | 25% |
| CW12MW | HastelloyC | ASTM-A494 | N30002 | 0.12 | 15.5-17.5 | balon | 16.0-18.0 | – | 4.5-7.5 | – | W-3.75-5.25, V-.20-.40 | 72 | 40 | 4% |
| CW12MW | Hastelloy C-276 | ASTM-A494 | N30002 | 0.02 | 15.5-17.5 | balon | 16.0-18.0 | – | 4.5-7.5 | – | W-3.75-5.25, V-.20-.40 | 72 | 40 | 4% |
| CY40 | Inconel 600 | ASTM-A494 | N06040 | 0.4 | 14.0-17.0 | balon | – | – | 11 | – | – | 70 | 28 | 30% |
| CZ100 | Níquel fundido | ASTM-A494 | N02100 | 1 | – | 95,0 min. | – | 1.25 | 3 | – | – | 50 | 18 | 10% |
| N7M | Hastelloy B Modificado | ASTM-A494 | N30007 | 0.07 | 1 | balon | 30.0-33.0 | – | 3 | – | – | 76 | 40 | 20% |
| N12MV | Hastelloy B | ASTM-A494 | N30012 | 0.12 | 1 | balon | 26.0-30.0 | – | 4.0-6.0 | – | – | 76 | 40 | 6% |
| M35-1 | monel 400 | ASTM-A494, A990 | N24135 | 0.35 | – | balon | – | 26.0-33.0 | 3.5 | 0.5 | Si 1,25 | 65 | 25 | 25% |
| M35-2 | Monel | ASTM-A494 | N04020 | 0.35 | – | balon | – | 26.0-33.0 | 3.5 | – | Sí 2.0 | 65 | 30 | 25% |
| M35-B/M30H | H-Monel | ASTM-A494, QQ-N-288 Comp. B | N24030 | 0.3 | – | balon | – | 27.0-33.0 | 2.5 | – | Sí 2,7-3,9 | 700 | 60 | 10% |
| M35-C | Monel | QQ-N-288 Comp C | N24025 | 0.2 | – | balon | – | 27.0-31.0 | 2.5 | – | Sí 3.3-3.7 | 120 | 80 | 10% |
| M35-D/M25S | S-Monel | ASTM A494, QQ-N-288 Comp D | N24025 | 0.25 | – | balon | – | 27.0-31.0 | 2.5 | – | Si 3,5-4,5 | – | – | – |
| M30C / M35W | Monel soldable | ASTM-A494, QQ-N-288 Comp E | N24130 | 0.3 | – | balon | – | 26.0-33.0 | 3.5 | – | Si 1,0-2,0, Cb 1,0-3,0 | 65 | 32.5 | 25% |
| 952 | Al Bronce Grado A | ASTM-B148 | C95200 | – | – | – | – | 86,0 minutos | 2.5-4.0 | – | Al 8,5-9,5 | 65 | 25 | 20% |
| 954 | Aluminio-Bronce | ASTM-B148 | C95400 | – | – | 1,5 máx. | – | 83,0 minutos | 3.0-5.0 | – | Al 10,0-11,5 | 75 | 30 | 12% |
| 955 | Aluminio-Bronce | ASTM-B148 | C95500 | – | – | 3.0-5.5 | – | 78,0 minutos | 3.0-5.0 | – | Al 10,0-11,5 | 90 | 40 | 6% |
| 958 | Ni-Al-Brz | ASTM-B148 | C95800 | – | – | 4.0-5.0 | – | 79,0 mín. | 3.0-4.5 | – | Al 8.5-9.5 Pb .03 máx. | 85 | 35 | 15% |
| 964 | 70*30 Cobre-Níquel | ASTM-B369 | C96400 | 0.15 | – | 28.0-32.0 | – | balon | .25-1.5 | 0.5-1.5 | mn 1,5 | 60 | 32 | 20% |
| CD4MCuN | Dúplex Grado 1B | ASTM-A890, A995 | J93372 | 0.04 | 24.5-26.5 | 4.75-6.0 | 1.75-2.25 | 2.75-3.25 | balon | – | 0,10-0,25 | 100 | 70 | 16% |
| CD3MCuN | Dúplex Grado 1C | ASTM-A890 | J93373 | 0.03 | 24-26.7 | 5.6-6.7 | 2.9-3.8 | 1.4-1.9 | balon | – | 0,22-0,33 | 100 | 65 | 25% |
| CE8MN | Dúplex Grado 2A | ASTM-A351, A890, A995 | J93345 | 0.08 | 22.5-25.5 | 8.0-11.0 | 3.00-4.50 | – | balon | – | 0,10-0,30 | 95 | 65 | 25% |
| CD6MN | Dúplex Grado 3A | ASTM-A890, A995 | J93371 | 0.06 | 24.0-27.0 | 4.0-6.0 | 1.75-2.50 | – | balon | – | 0,10-0,25 | 95 | 65 | 25% |
| CD3MN | Dúplex Grado 4A | ASTM-A890, A995 | J92205 | 0.03 | 21.0-23.5 | 4.5-6.5 | 2.5-3.5 | 1,00 máximo | balon | – | 0,10-0,30 | 90 | 60 | 25% |
| CE3MN | Dúplex Grado 5A | ASTM-A890, A995 | J93404 | 0.03 | 24.0-26.0 | 6.0-8.0 | 4.0-5.0 | – | balon | – | 0,10-0,03 | 100 | 75 | 18% |
| CD3MWCuN | Grado 6A Zeron100 | ASTM-A890, A995 | J93380 | 0.03 | 24.0-26.0 | 6.5-8.5 | 3.0-4.0 | 0.5-1.0 | balon | – | N 0,02-0,03 W 0,5-1,0 | 100 | 65 | 25% |
| S.S | ASTM-A297 | ASTM-A297 | J93503 | 0.20-0.50 | 24.0-28.0 | 11.0-14.0 | 0.5 | 1 | balon | – | – | 75 | 35 | 10% |
| Hong Kong | ASTM-A297 | ASTM-A297 | J94224 | 0.20-0.60 | 24.0-28.0 | 18.0-22.0 | 0.5 | 1 | balon | – | – | 65 | 35 | 10% |
| hn | HI-35 | ASTM-A297 | J94213 | 0.20-0.50 | 19.0-23.0 | 23.0-27.0 | 0.5 | 1 | balon | – | – | 63 | – | 8% |
| HT | 330 (15-35) | ASTM-A297 | N08605 | 0.35-0.75 | 15.0-19.0 | 33.0-37.0 | 0.5 | 1 | balon | – | – | 65 | – | 4% |
| HU | (19-39) | ASTM-A297 | N08004 | 0.35-0.75 | 17.0-21.0 | 37.0-41.0 | 0.5 | 1 | balon | – | – | 65 | – | 4% |
| HX | ACI HX | ASTM-A297 | N06006 | 0.35-0.75 | 15.0-19.0 | 64.0-68.0 | 0.5 | 1 | balon | – | – | 60 | – | – |
| WCA | Acero carbono | ASTM-A216 | J02502 | 0.25 | 0.5 | 0.5 | 0.2 | 0.3 | balon | – | – | 60-85 | 30 | 24% |
| WCB | Acero carbono | ASTM-A216 | J03002 | 0.3 | 0.5 | 0.5 | 0.2 | 0.3 | balon | – | – | 70-95 | 36 | 22% |
| CMI | Acero carbono | ASTM-A216 | J02503 | 0.25 | 0.5 | 0.5 | 0.2 | 0.3 | balon | – | – | 70-95 | 40 | 22% |
| LCB | Acero carbono | ASTM-A352 | J03003 | 0.3 | 0.5 | 0.5 | 0.2 | 0.3 | balon | – | – | 65 | 35 | 24% |
| LCC | Acero carbono | ASTM-A352 | J02505 | 0.25 | 0.5 | 0.5 | 0.2 | 0.3 | balon | – | – | 70 | 40 | 22% |
| LC2 | ASTM-A352 | J22500 | 0.25 | – | 2.00-3.00 | 0.45-0.65 | – | balon | – | – | 70.0-95.0 | 40.0 | 24% | |
| LC3 | ASTM-A352 | J31550 | 0.15 | – | 3.00-4.00 | – | – | balon | – | – | 70.0-95.0 | 40.0 | 24% | |
| WC6 | ASTM-A217 | J12072 | 0.05-0.20 | 1.00-1.50 | – | 0.45-0.65 | 0.50 | balon | – | – | 70-95 | 40 | 20% | |
| WC9 | ASTM-A217 | J21890 | 0.05-0.18 | 2.00-2.75 | – | 0.90-1.20 | 0.50 | balon | – | – | 70-95 | 40 | 20% | |
| C5 | ASTM-A217 | J42045 | 0.20 | 4.00-6.50 | – | 0.45-0.65 | 0.50 | balon | – | – | 90-115 | 60 | 18% | |
| C12 | ASTM-A217 | J82090 | 0.20 | 8.00-10.00 | – | 0.90-1.20 | 0.50 | balon | – | – | 90-115 | 60 | 18% | |
| C12A | Grado 91 | ASTM-A217 | J84090 | 0.08-0.12 | 8.0-9.5 | 0.40 | 0.85-1.05 | – | balon | 0.060-0.10 | N 0,030-0,070, V 0,18-0,25 | 85-110 | 60 | 18% |
| SC8625 | ASTM A487, A148 | 0.30 | 0.40-0.80 | 0.40-0.80 | 0.15-0.30 | 0.50 | balon | – | – | 105-130 | 85 | 17% |
Hastelloy C276 (ASTM A 494, grado CW12MW)
Las válvulas de instrumentación Hastelloy C276 de alto rendimiento tienen una resistencia superior a varios ácidos. Por ejemplo, las válvulas de bola Hastelloy C276 tienen la capacidad de resistir ácidos como el ácido sulfúrico, clorhídrico, fluorhídrico, nítrico y crómico. La válvula de bola Hastelloy incluso tiene una buena resistencia a la corrosión localizada.
CW12MW es la antigua aleación fundida original de Hastelloy C. Su límite de carbono más alto de 0,12% como máximo junto con sus niveles más altos de hierro y tungsteno hacen que esta aleación sea inferior a cualquiera de los otros grados en resistencia a la corrosión y ductilidad. CW12MW no es el equivalente fundido para UNS N10276.
CW6M
CW6M es la siguiente aleación fundida de Ni-Cr-Mo desarrollada. Se introdujo en 1949, por lo que esta aleación tiene una larga y exitosa historia. Si bien tiene un límite permitido de carbono y silicio más alto que los tipos C más nuevos que se enumeran a continuación, generalmente se fabrica con niveles de carbono y silicio mucho más bajos, lo que le otorga una buena resistencia a la corrosión tanto de los ácidos oxidantes como de los reductores.
CW2M
CW2M es el equivalente fundido de UNS N06455 desarrollado en 1976 para proporcionar una mejor estabilidad metalúrgica que UNS N10276 a altas temperaturas. Un beneficio adicional fue que es un mejor grado de fundición que el CW12MW. Su rendimiento mejorado con respecto a CW12MW fue el resultado de cantidades reducidas de fases intermetálicas en su microestructura. Esto se logró reduciendo sus niveles de carbono, silicio, hierro, cromo y molibdeno y eliminando la adición de tungsteno.
CX2MW
CX2MW es el equivalente fundido de UNS N06022. Esta aleación tiene un mayor contenido de cromo, pero un menor contenido de molibdeno que las otras aleaciones tipo Hastelloy C. El mayor contenido de cromo le da a esta aleación una mejor resistencia a la corrosión en ambientes oxidantes calientes como lejía y salmueras cloradas. Sin embargo, el menor contenido de molibdeno sacrifica cierta resistencia a los servicios reductores donde estas aleaciones también se usan comúnmente, por ejemplo, ácidos sulfúrico y clorhídrico.
CX2M
CX2M es el equivalente fundido a UNS N06059. Tiene una cantidad ligeramente mayor de cromo y molibdeno que CX2MW. El mayor contenido de cromo puede proporcionar una buena resistencia a servicios oxidantes fuertes y su mayor contenido de molibdeno puede proporcionar una buena resistencia a los ácidos sulfúrico y clorhídrico.
UNS N06200
UNS N06200 (Hastelloy C-2000) es la aleación tipo C más nueva, pero solo está disponible como componente forjado porque su contenido extremadamente bajo de carbono y silicio significa que no es beneficioso para fabricar una aleación fundida. UNS N06200 contiene un contenido de cromo similar al UNS N06022, pero tiene más molibdeno junto con una pequeña cantidad de cobre. El mayor contenido de molibdeno junto con el cobre le da a la aleación una mejor resistencia a los ácidos reductores como el sulfúrico y el clorhídrico.
Etiquetas relacionadas :
Diez artículos antes y después
Spanish 
English 
German 
French 
Russian 
Portuguese 
Turkish