{"id":9446,"date":"2021-12-30T08:11:39","date_gmt":"2021-12-30T08:11:39","guid":{"rendered":"https:\/\/zecovalve.com\/hastelloy-c276-high-pressure-seal-gate-valvea494-cw12mw-gate-valve6-900lb-gate-valve-titanium-ball-valves-supplier-chinacryogenic-globe-valve-manufacturers-chinac95800-butterfly-valve-in-china.html"},"modified":"2022-09-17T12:07:34","modified_gmt":"2022-09-17T12:07:34","slug":"hastelloy-c276-high-pressure-seal-gate-valvea494-cw12mw-gate-valve6-900lb-gate-valve-titanium-ball-valves-supplier-chinacryogenic-globe-valve-manufacturers-chinac95800-butterfly-valve-in-china","status":"publish","type":"post","link":"https:\/\/zecovalve.com\/es\/hastelloy-c276-high-pressure-seal-gate-valvea494-cw12mw-gate-valve6-900lb-gate-valve-titanium-ball-valves-supplier-chinacryogenic-globe-valve-manufacturers-chinac95800-butterfly-valve-in-china.html","title":{"rendered":"Hastelloy C276 (ASTM A 494, grado CW12MW)"},"content":{"rendered":"

METALURGIA DE MATERIALES DE FUNDICI\u00d3N DE V\u00c1LVULAS COMUNES<\/h2>\n\n\n\n
Aleaci\u00f3n fundida<\/th>Designaci\u00f3n forjada similar<\/th>Especificaci\u00f3n<\/th>UNS No.<\/th>C<\/th>cr<\/th>Ni<\/th>Mes<\/th>Cu<\/th>fe<\/th>cb<\/th>Otro<\/th>Tracci\u00f3n (ksi)<\/th>Rendimiento (ksi)<\/th>elong<\/th><\/tr>
CA6NM<\/td>415, F6NM<\/td>ASTM-A743, A487<\/td>J91540<\/td>0.06<\/td>11.5-14.0<\/td>3.5-4.5<\/td>.4-1.0<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>110<\/td>80<\/td>17%<\/td><\/tr>
CA15<\/td>410<\/td>ASTM-A217, A743<\/td>J91150<\/td>0.15<\/td>11.5-14.0<\/td>1<\/td>0.5<\/td>0.5<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>90<\/td>65<\/td>18%<\/td><\/tr>
CB7Cu-1<\/td>17-4PH<\/td>ASTM-A747, AMS-5398C<\/td>J92180<\/td>0.06<\/td>15.5-17.7<\/td>3.6-4.6<\/td>\u2013<\/td>2.5-3.2<\/td>balon<\/td>.15-.35<\/td>\u2013<\/td>135 H1100 Condici\u00f3n<\/td>100<\/td>9%<\/td><\/tr>
CF3<\/td>304L<\/td>ASTM-A351, A743, A744<\/td>J92500<\/td>0.03<\/td>17.0-21.0<\/td>8.0-12.0<\/td>0.5<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>70<\/td>30<\/td>35%<\/td><\/tr>
CF3MN<\/td>316LN<\/td>ASTM-A743, A351<\/td>J92804<\/td>0.03<\/td>17.0-21.0<\/td>9.0-13.0<\/td>2.0-3.0<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>N-0,10-0,20<\/td>75<\/td>37<\/td>35%<\/td><\/tr>
CF3M<\/td>316L<\/td>ASTM-A351, A743, A744<\/td>J92800<\/td>0.03<\/td>17.0-21.0<\/td>9.0-13.0<\/td>2.0-3.0<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>70<\/td>30<\/td>30%<\/td><\/tr>
CF8<\/td>304<\/td>ASTM-A351, A743, A744<\/td>J92600<\/td>0.08<\/td>18.0-21.0<\/td>8.0-11.0<\/td>0.5<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>70<\/td>30<\/td>35%<\/td><\/tr>
CF8C<\/td>347<\/td>ASTM-A351, A743, A744<\/td>J92710<\/td>0.08<\/td>18.0-21.0<\/td>9.0-12.0<\/td>0.5<\/td>\u2013<\/td>balon<\/td>8xC-1.0<\/td>\u2013<\/td>70<\/td>30<\/td>30%<\/td><\/tr>
CF8M<\/td>316<\/td>ASTM-A351, A743, A744<\/td>J92900<\/td>0.08<\/td>18.0-21.0<\/td>9.0-12.0<\/td>2.0-3.0<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>70<\/td>30<\/td>30%<\/td><\/tr>
CG3M<\/td>317L<\/td>ASTM-A351, A743, A744<\/td>J92999<\/td>0.03<\/td>18.0-21.0<\/td>9.0-13.0<\/td>3.0-4.0<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>75<\/td>35<\/td>25%<\/td><\/tr>
CG8M<\/td>317<\/td>ASTM-A351, A743, A744<\/td>J93000<\/td>0.08<\/td>18.0-21.0<\/td>9.0-13.0<\/td>3.0-4.0<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>75<\/td>35<\/td>25%<\/td><\/tr>
CN7M<\/td>Aleaci\u00f3n 20<\/td>ASTM-A351, A743, A744<\/td>N08007<\/td>0.07<\/td>19.0-22.0<\/td>27.5-30.5<\/td>2.0-3.0<\/td>3.0-4.0<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>62<\/td>25<\/td>35%<\/td><\/tr>
CN2MCuN<\/td>904L<\/td><\/td>N08904<\/td>0.02<\/td>19.0-23.0<\/td>23.0-28.0<\/td>4.0-5.0<\/td>1.0-2.0<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>65<\/td>28<\/td>35%<\/td><\/tr>
CK3MCuN<\/td>Avesta 254-SMO<\/td>ASTM-A351, A743, A744<\/td>J93254<\/td>0.025<\/td>19.5-20.5<\/td>17.5-19.5<\/td>6.00-7.00<\/td>0.50-1.00<\/td>balon<\/td>\u2013<\/td>0,18-0,24<\/td>80<\/td>38<\/td>35%<\/td><\/tr>
CN3MN<\/td>AL6XN<\/td>ASTM-A351, A743, A744<\/td>J94651<\/td>0.030<\/td>20.0-22.0<\/td>23.5-25.5<\/td>6.0-7.0<\/td>0.75<\/td>balon<\/td>\u2013<\/td>0,18-1,26<\/td>80<\/td>38<\/td>35%<\/td><\/tr>
CX2MW<\/td>Hastelloy C-22<\/td>ASTM A494<\/td>N26022<\/td>0.02<\/td>20.0-22.5<\/td>balon<\/td>12.5-14.5<\/td>\u2013<\/td>2.0-6.0<\/td>\u2013<\/td>W-2.5-3.5<\/td>80<\/td>45<\/td>30%<\/td><\/tr>
CW2M<\/td>Hastelloy C4C<\/td>ASTM-A494, A990<\/td>N26455<\/td>0.02<\/td>15.0-17.5<\/td>balon<\/td>15.0-17.5<\/td>\u2013<\/td>2<\/td>\u2013<\/td>\u2013<\/td>72<\/td>40<\/td>20%<\/td><\/tr>
CW6M<\/td>Hastelloy C Modificado<\/td>ASTM-A494<\/td>N30107<\/td>0.07<\/td>17.0-20.0<\/td>balon<\/td>17.0-20.0<\/td>\u2013<\/td>3<\/td>\u2013<\/td>\u2013<\/td>72<\/td>40<\/td>25%<\/td><\/tr>
CW6MC<\/td>Inconel 625<\/td>ASTM-A494, MIL-C-24615<\/td>N26625<\/td>0.06<\/td>20.0-23.0<\/td>balon<\/td>8.0-10.0<\/td>\u2013<\/td>5<\/td>3.15-4.5<\/td>\u2013<\/td>70<\/td>40<\/td>25%<\/td><\/tr>
CW12MW<\/td>HastelloyC<\/td>ASTM-A494<\/td>N30002<\/td>0.12<\/td>15.5-17.5<\/td>balon<\/td>16.0-18.0<\/td>\u2013<\/td>4.5-7.5<\/td>\u2013<\/td>W-3.75-5.25, V-.20-.40<\/td>72<\/td>40<\/td>4%<\/td><\/tr>
CW12MW<\/td>Hastelloy C-276<\/td>ASTM-A494<\/td>N30002<\/td>0.02<\/td>15.5-17.5<\/td>balon<\/td>16.0-18.0<\/td>\u2013<\/td>4.5-7.5<\/td>\u2013<\/td>W-3.75-5.25, V-.20-.40<\/td>72<\/td>40<\/td>4%<\/td><\/tr>
CY40<\/td>Inconel 600<\/td>ASTM-A494<\/td>N06040<\/td>0.4<\/td>14.0-17.0<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>11<\/td>\u2013<\/td>\u2013<\/td>70<\/td>28<\/td>30%<\/td><\/tr>
CZ100<\/td>N\u00edquel fundido<\/td>ASTM-A494<\/td>N02100<\/td>1<\/td>\u2013<\/td>95,0 min.<\/td>\u2013<\/td>1.25<\/td>3<\/td>\u2013<\/td>\u2013<\/td>50<\/td>18<\/td>10%<\/td><\/tr>
N7M<\/td>Hastelloy B Modificado<\/td>ASTM-A494<\/td>N30007<\/td>0.07<\/td>1<\/td>balon<\/td>30.0-33.0<\/td>\u2013<\/td>3<\/td>\u2013<\/td>\u2013<\/td>76<\/td>40<\/td>20%<\/td><\/tr>
N12MV<\/td>Hastelloy B<\/td>ASTM-A494<\/td>N30012<\/td>0.12<\/td>1<\/td>balon<\/td>26.0-30.0<\/td>\u2013<\/td>4.0-6.0<\/td>\u2013<\/td>\u2013<\/td>76<\/td>40<\/td>6%<\/td><\/tr>
M35-1<\/td>monel 400<\/td>ASTM-A494, A990<\/td>N24135<\/td>0.35<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>26.0-33.0<\/td>3.5<\/td>0.5<\/td>Si 1,25<\/td>65<\/td>25<\/td>25%<\/td><\/tr>
M35-2<\/td>Monel<\/td>ASTM-A494<\/td>N04020<\/td>0.35<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>26.0-33.0<\/td>3.5<\/td>\u2013<\/td>S\u00ed 2.0<\/td>65<\/td>30<\/td>25%<\/td><\/tr>
M35-B\/M30H<\/td>H-Monel<\/td>ASTM-A494, QQ-N-288 Comp. B<\/td>N24030<\/td>0.3<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>27.0-33.0<\/td>2.5<\/td>\u2013<\/td>S\u00ed 2,7-3,9<\/td>700<\/td>60<\/td>10%<\/td><\/tr>
M35-C<\/td>Monel<\/td>QQ-N-288 Comp C<\/td>N24025<\/td>0.2<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>27.0-31.0<\/td>2.5<\/td>\u2013<\/td>S\u00ed 3.3-3.7<\/td>120<\/td>80<\/td>10%<\/td><\/tr>
M35-D\/M25S<\/td>S-Monel<\/td>ASTM A494, QQ-N-288 Comp D<\/td>N24025<\/td>0.25<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>27.0-31.0<\/td>2.5<\/td>\u2013<\/td>Si 3,5-4,5<\/td>\u2013<\/td>\u2013<\/td>\u2013<\/td><\/tr>
M30C \/ M35W<\/td>Monel soldable<\/td>ASTM-A494, QQ-N-288 Comp E<\/td>N24130<\/td>0.3<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>26.0-33.0<\/td>3.5<\/td>\u2013<\/td>Si 1,0-2,0, Cb 1,0-3,0<\/td>65<\/td>32.5<\/td>25%<\/td><\/tr>
952<\/td>Al Bronce Grado A<\/td>ASTM-B148<\/td>C95200<\/td>\u2013<\/td>\u2013<\/td>\u2013<\/td>\u2013<\/td>86,0 minutos<\/td>2.5-4.0<\/td>\u2013<\/td>Al 8,5-9,5<\/td>65<\/td>25<\/td>20%<\/td><\/tr>
954<\/td>Aluminio-Bronce<\/td>ASTM-B148<\/td>C95400<\/td>\u2013<\/td>\u2013<\/td>1,5 m\u00e1x.<\/td>\u2013<\/td>83,0 minutos<\/td>3.0-5.0<\/td>\u2013<\/td>Al 10,0-11,5<\/td>75<\/td>30<\/td>12%<\/td><\/tr>
955<\/td>Aluminio-Bronce<\/td>ASTM-B148<\/td>C95500<\/td>\u2013<\/td>\u2013<\/td>3.0-5.5<\/td>\u2013<\/td>78,0 minutos<\/td>3.0-5.0<\/td>\u2013<\/td>Al 10,0-11,5<\/td>90<\/td>40<\/td>6%<\/td><\/tr>
958<\/td>Ni-Al-Brz<\/td>ASTM-B148<\/td>C95800<\/td>\u2013<\/td>\u2013<\/td>4.0-5.0<\/td>\u2013<\/td>79,0 m\u00edn.<\/td>3.0-4.5<\/td>\u2013<\/td>Al 8.5-9.5 Pb .03 m\u00e1x.<\/td>85<\/td>35<\/td>15%<\/td><\/tr>
964<\/td>70*30 Cobre-N\u00edquel<\/td>ASTM-B369<\/td>C96400<\/td>0.15<\/td>\u2013<\/td>28.0-32.0<\/td>\u2013<\/td>balon<\/td>.25-1.5<\/td>0.5-1.5<\/td>mn 1,5<\/td>60<\/td>32<\/td>20%<\/td><\/tr>
CD4MCuN<\/td>D\u00faplex Grado 1B<\/td>ASTM-A890, A995<\/td>J93372<\/td>0.04<\/td>24.5-26.5<\/td>4.75-6.0<\/td>1.75-2.25<\/td>2.75-3.25<\/td>balon<\/td>\u2013<\/td>0,10-0,25<\/td>100<\/td>70<\/td>16%<\/td><\/tr>
CD3MCuN<\/td>D\u00faplex Grado 1C<\/td>ASTM-A890<\/td>J93373<\/td>0.03<\/td>24-26.7<\/td>5.6-6.7<\/td>2.9-3.8<\/td>1.4-1.9<\/td>balon<\/td>\u2013<\/td>0,22-0,33<\/td>100<\/td>65<\/td>25%<\/td><\/tr>
CE8MN<\/td>D\u00faplex Grado 2A<\/td>ASTM-A351, A890, A995<\/td>J93345<\/td>0.08<\/td>22.5-25.5<\/td>8.0-11.0<\/td>3.00-4.50<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>0,10-0,30<\/td>95<\/td>65<\/td>25%<\/td><\/tr>
CD6MN<\/td>D\u00faplex Grado 3A<\/td>ASTM-A890, A995<\/td>J93371<\/td>0.06<\/td>24.0-27.0<\/td>4.0-6.0<\/td>1.75-2.50<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>0,10-0,25<\/td>95<\/td>65<\/td>25%<\/td><\/tr>
CD3MN<\/td>D\u00faplex Grado 4A<\/td>ASTM-A890, A995<\/td>J92205<\/td>0.03<\/td>21.0-23.5<\/td>4.5-6.5<\/td>2.5-3.5<\/td>1,00 m\u00e1ximo<\/td>balon<\/td>\u2013<\/td>0,10-0,30<\/td>90<\/td>60<\/td>25%<\/td><\/tr>
CE3MN<\/td>D\u00faplex Grado 5A<\/td>ASTM-A890, A995<\/td>J93404<\/td>0.03<\/td>24.0-26.0<\/td>6.0-8.0<\/td>4.0-5.0<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>0,10-0,03<\/td>100<\/td>75<\/td>18%<\/td><\/tr>
CD3MWCuN<\/td>Grado 6A Zeron100<\/td>ASTM-A890, A995<\/td>J93380<\/td>0.03<\/td>24.0-26.0<\/td>6.5-8.5<\/td>3.0-4.0<\/td>0.5-1.0<\/td>balon<\/td>\u2013<\/td>N 0,02-0,03 W 0,5-1,0<\/td>100<\/td>65<\/td>25%<\/td><\/tr>
S.S<\/td>ASTM-A297<\/td>ASTM-A297<\/td>J93503<\/td>0.20-0.50<\/td>24.0-28.0<\/td>11.0-14.0<\/td>0.5<\/td>1<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>75<\/td>35<\/td>10%<\/td><\/tr>
Hong Kong<\/td>ASTM-A297<\/td>ASTM-A297<\/td>J94224<\/td>0.20-0.60<\/td>24.0-28.0<\/td>18.0-22.0<\/td>0.5<\/td>1<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>65<\/td>35<\/td>10%<\/td><\/tr>
hn<\/td>HI-35<\/td>ASTM-A297<\/td>J94213<\/td>0.20-0.50<\/td>19.0-23.0<\/td>23.0-27.0<\/td>0.5<\/td>1<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>63<\/td>\u2013<\/td>8%<\/td><\/tr>
HT<\/td>330 (15-35)<\/td>ASTM-A297<\/td>N08605<\/td>0.35-0.75<\/td>15.0-19.0<\/td>33.0-37.0<\/td>0.5<\/td>1<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>65<\/td>\u2013<\/td>4%<\/td><\/tr>
HU<\/td>(19-39)<\/td>ASTM-A297<\/td>N08004<\/td>0.35-0.75<\/td>17.0-21.0<\/td>37.0-41.0<\/td>0.5<\/td>1<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>65<\/td>\u2013<\/td>4%<\/td><\/tr>
HX<\/td>ACI HX<\/td>ASTM-A297<\/td>N06006<\/td>0.35-0.75<\/td>15.0-19.0<\/td>64.0-68.0<\/td>0.5<\/td>1<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>60<\/td>\u2013<\/td>\u2013<\/td><\/tr>
WCA<\/td>Acero carbono<\/td>ASTM-A216<\/td>J02502<\/td>0.25<\/td>0.5<\/td>0.5<\/td>0.2<\/td>0.3<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>60-85<\/td>30<\/td>24%<\/td><\/tr>
WCB<\/td>Acero carbono<\/td>ASTM-A216<\/td>J03002<\/td>0.3<\/td>0.5<\/td>0.5<\/td>0.2<\/td>0.3<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>70-95<\/td>36<\/td>22%<\/td><\/tr>
CMI<\/td>Acero carbono<\/td>ASTM-A216<\/td>J02503<\/td>0.25<\/td>0.5<\/td>0.5<\/td>0.2<\/td>0.3<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>70-95<\/td>40<\/td>22%<\/td><\/tr>
LCB<\/td>Acero carbono<\/td>ASTM-A352<\/td>J03003<\/td>0.3<\/td>0.5<\/td>0.5<\/td>0.2<\/td>0.3<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>65<\/td>35<\/td>24%<\/td><\/tr>
LCC<\/td>Acero carbono<\/td>ASTM-A352<\/td>J02505<\/td>0.25<\/td>0.5<\/td>0.5<\/td>0.2<\/td>0.3<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>70<\/td>40<\/td>22%<\/td><\/tr>
LC2<\/td><\/td>ASTM-A352<\/td>J22500<\/td>0.25<\/td>\u2013<\/td>2.00-3.00<\/td>0.45-0.65<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>70.0-95.0<\/td>40.0<\/td>24%<\/td><\/tr>
LC3<\/td><\/td>ASTM-A352<\/td>J31550<\/td>0.15<\/td>\u2013<\/td>3.00-4.00<\/td>\u2013<\/td>\u2013<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>70.0-95.0<\/td>40.0<\/td>24%<\/td><\/tr>
WC6<\/td><\/td>ASTM-A217<\/td>J12072<\/td>0.05-0.20<\/td>1.00-1.50<\/td>\u2013<\/td>0.45-0.65<\/td>0.50<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>70-95<\/td>40<\/td>20%<\/td><\/tr>
WC9<\/td><\/td>ASTM-A217<\/td>J21890<\/td>0.05-0.18<\/td>2.00-2.75<\/td>\u2013<\/td>0.90-1.20<\/td>0.50<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>70-95<\/td>40<\/td>20%<\/td><\/tr>
C5<\/td><\/td>ASTM-A217<\/td>J42045<\/td>0.20<\/td>4.00-6.50<\/td>\u2013<\/td>0.45-0.65<\/td>0.50<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>90-115<\/td>60<\/td>18%<\/td><\/tr>
C12<\/td><\/td>ASTM-A217<\/td>J82090<\/td>0.20<\/td>8.00-10.00<\/td>\u2013<\/td>0.90-1.20<\/td>0.50<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>90-115<\/td>60<\/td>18%<\/td><\/tr>
C12A<\/td>Grado 91<\/td>ASTM-A217<\/td>J84090<\/td>0.08-0.12<\/td>8.0-9.5<\/td>0.40<\/td>0.85-1.05<\/td>\u2013<\/td>balon<\/td>0.060-0.10<\/td>N 0,030-0,070, V 0,18-0,25<\/td>85-110<\/td>60<\/td>18%<\/td><\/tr>
SC8625<\/td><\/td>ASTM A487, A148<\/td><\/td>0.30<\/td>0.40-0.80<\/td>0.40-0.80<\/td>0.15-0.30<\/td>0.50<\/td>balon<\/td>\u2013<\/td>\u2013<\/td>105-130<\/td>85<\/td>17%<\/td><\/tr><\/tbody><\/table><\/figure>\n\n\n\n

Hastelloy C276 (ASTM A 494, grado CW12MW)<\/h2>\n\n\n\n

Las v\u00e1lvulas de instrumentaci\u00f3n Hastelloy C276 de alto rendimiento tienen una resistencia superior a varios \u00e1cidos. Por ejemplo, las v\u00e1lvulas de bola Hastelloy C276 tienen la capacidad de resistir \u00e1cidos como el \u00e1cido sulf\u00farico, clorh\u00eddrico, fluorh\u00eddrico, n\u00edtrico y cr\u00f3mico. La v\u00e1lvula de bola Hastelloy incluso tiene una buena resistencia a la corrosi\u00f3n localizada.<\/p>\n\n\n\n

CW12MW es la antigua aleaci\u00f3n fundida original de Hastelloy C. Su l\u00edmite de carbono m\u00e1s alto de 0,12% como m\u00e1ximo junto con sus niveles m\u00e1s altos de hierro y tungsteno hacen que esta aleaci\u00f3n sea inferior a cualquiera de los otros grados en resistencia a la corrosi\u00f3n y ductilidad. CW12MW no es el equivalente fundido para UNS N10276.<\/p>\n\n\n\n

CW6M<\/h2>\n\n\n\n

CW6M es la siguiente aleaci\u00f3n fundida de Ni-Cr-Mo desarrollada. Se introdujo en 1949, por lo que esta aleaci\u00f3n tiene una larga y exitosa historia. Si bien tiene un l\u00edmite permitido de carbono y silicio m\u00e1s alto que los tipos C m\u00e1s nuevos que se enumeran a continuaci\u00f3n, generalmente se fabrica con niveles de carbono y silicio mucho m\u00e1s bajos, lo que le otorga una buena resistencia a la corrosi\u00f3n tanto de los \u00e1cidos oxidantes como de los reductores.<\/p>\n\n\n\n

CW2M<\/h2>\n\n\n\n

CW2M es el equivalente fundido de UNS N06455 desarrollado en 1976 para proporcionar una mejor estabilidad metal\u00fargica que UNS N10276 a altas temperaturas. Un beneficio adicional fue que es un mejor grado de fundici\u00f3n que el CW12MW. Su rendimiento mejorado con respecto a CW12MW fue el resultado de cantidades reducidas de fases intermet\u00e1licas en su microestructura. Esto se logr\u00f3 reduciendo sus niveles de carbono, silicio, hierro, cromo y molibdeno y eliminando la adici\u00f3n de tungsteno.<\/p>\n\n\n\n

CX2MW<\/h2>\n\n\n\n

CX2MW es el equivalente fundido de UNS N06022. Esta aleaci\u00f3n tiene un mayor contenido de cromo, pero un menor contenido de molibdeno que las otras aleaciones tipo Hastelloy C. El mayor contenido de cromo le da a esta aleaci\u00f3n una mejor resistencia a la corrosi\u00f3n en ambientes oxidantes calientes como lej\u00eda y salmueras cloradas. Sin embargo, el menor contenido de molibdeno sacrifica cierta resistencia a los servicios reductores donde estas aleaciones tambi\u00e9n se usan com\u00fanmente, por ejemplo, \u00e1cidos sulf\u00farico y clorh\u00eddrico.<\/p>\n\n\n\n

CX2M<\/h2>\n\n\n\n

CX2M es el equivalente fundido a UNS N06059. Tiene una cantidad ligeramente mayor de cromo y molibdeno que CX2MW. El mayor contenido de cromo puede proporcionar una buena resistencia a servicios oxidantes fuertes y su mayor contenido de molibdeno puede proporcionar una buena resistencia a los \u00e1cidos sulf\u00farico y clorh\u00eddrico.<\/p>\n\n\n\n

UNS N06200<\/h2>\n\n\n\n

UNS N06200 (Hastelloy C-2000) es la aleaci\u00f3n tipo C m\u00e1s nueva, pero solo est\u00e1 disponible como componente forjado porque su contenido extremadamente bajo de carbono y silicio significa que no es beneficioso para fabricar una aleaci\u00f3n fundida. UNS N06200 contiene un contenido de cromo similar al UNS N06022, pero tiene m\u00e1s molibdeno junto con una peque\u00f1a cantidad de cobre. El mayor contenido de molibdeno junto con el cobre le da a la aleaci\u00f3n una mejor resistencia a los \u00e1cidos reductores como el sulf\u00farico y el clorh\u00eddrico.<\/p>\n\n\n\n\n