METALURGIA DE MATERIAIS DE FUNDIÇÃO DE VÁLVULAS COMUNS
| Liga fundida | Designação Forjada Semelhante | Especificação | UNS Não. | C | Cr | Não | Mo | Cu | Fé | Cb | Outro | Tração (ksi) | Rendimento (ksi) | Alongar |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| CA6NM | 415, F6NM | ASTM-A743, A487 | J91540 | 0.06 | 11.5-14.0 | 3.5-4.5 | .4-1.0 | – | BAL | – | – | 110 | 80 | 17% |
| CA15 | 410 | ASTM-A217, A743 | J91150 | 0.15 | 11.5-14.0 | 1 | 0.5 | 0.5 | BAL | – | – | 90 | 65 | 18% |
| CB7Cu-1 | 17-4PH | ASTM-A747, AMS-5398C | J92180 | 0.06 | 15.5-17.7 | 3.6-4.6 | – | 2.5-3.2 | BAL | .15-.35 | – | 135 H1100 Condição | 100 | 9% |
| CF3 | 304L | ASTM-A351, A743, A744 | J92500 | 0.03 | 17.0-21.0 | 8.0-12.0 | 0.5 | – | BAL | – | – | 70 | 30 | 35% |
| CF3MN | 316LN | ASTM-A743, A351 | J92804 | 0.03 | 17.0-21.0 | 9.0-13.0 | 2.0-3.0 | – | BAL | – | N-0,10-0,20 | 75 | 37 | 35% |
| CF3M | 316L | ASTM-A351, A743, A744 | J92800 | 0.03 | 17.0-21.0 | 9.0-13.0 | 2.0-3.0 | – | BAL | – | – | 70 | 30 | 30% |
| CF8 | 304 | ASTM-A351, A743, A744 | J92600 | 0.08 | 18.0-21.0 | 8.0-11.0 | 0.5 | – | BAL | – | – | 70 | 30 | 35% |
| CF8C | 347 | ASTM-A351, A743, A744 | J92710 | 0.08 | 18.0-21.0 | 9.0-12.0 | 0.5 | – | BAL | 8xC-1.0 | – | 70 | 30 | 30% |
| CF8M | 316 | ASTM-A351, A743, A744 | J92900 | 0.08 | 18.0-21.0 | 9.0-12.0 | 2.0-3.0 | – | BAL | – | – | 70 | 30 | 30% |
| CG3M | 317L | ASTM-A351, A743, A744 | J92999 | 0.03 | 18.0-21.0 | 9.0-13.0 | 3.0-4.0 | – | BAL | – | – | 75 | 35 | 25% |
| CG8M | 317 | ASTM-A351, A743, A744 | J93000 | 0.08 | 18.0-21.0 | 9.0-13.0 | 3.0-4.0 | – | BAL | – | – | 75 | 35 | 25% |
| CN7M | Liga 20 | ASTM-A351, A743, A744 | N08007 | 0.07 | 19.0-22.0 | 27.5-30.5 | 2.0-3.0 | 3.0-4.0 | BAL | – | – | 62 | 25 | 35% |
| CN2MCuN | 904L | N08904 | 0.02 | 19.0-23.0 | 23.0-28.0 | 4.0-5.0 | 1.0-2.0 | BAL | – | – | 65 | 28 | 35% | |
| CK3MCuN | Avesta 254-SMO | ASTM-A351, A743, A744 | J93254 | 0.025 | 19.5-20.5 | 17.5-19.5 | 6.00-7.00 | 0.50-1.00 | BAL | – | N 0,18-0,24 | 80 | 38 | 35% |
| CN3MN | AL6XN | ASTM-A351, A743, A744 | J94651 | 0.030 | 20.0-22.0 | 23.5-25.5 | 6.0-7.0 | 0.75 | BAL | – | N 0,18-1,26 | 80 | 38 | 35% |
| CX2MW | Hastelloy C-22 | ASTM A494 | N26022 | 0.02 | 20.0-22.5 | BAL | 12.5-14.5 | – | 2.0-6.0 | – | W-2,5-3,5 | 80 | 45 | 30% |
| CW2M | Hastelloy C4C | ASTM-A494, A990 | N26455 | 0.02 | 15.0-17.5 | BAL | 15.0-17.5 | – | 2 | – | – | 72 | 40 | 20% |
| CW6M | Hastelloy C modificado | ASTM-A494 | N30107 | 0.07 | 17.0-20.0 | BAL | 17.0-20.0 | – | 3 | – | – | 72 | 40 | 25% |
| CW6MC | Inconel 625 | ASTM-A494, MIL-C-24615 | N26625 | 0.06 | 20.0-23.0 | BAL | 8.0-10.0 | – | 5 | 3.15-4.5 | – | 70 | 40 | 25% |
| CW12MW | Hastelloy C. | ASTM-A494 | N30002 | 0.12 | 15.5-17.5 | BAL | 16.0-18.0 | – | 4.5-7.5 | – | W-3,75-5,25, V-.20-.40 | 72 | 40 | 4% |
| CW12MW | Hastelloy C-276 | ASTM-A494 | N30002 | 0.02 | 15.5-17.5 | BAL | 16.0-18.0 | – | 4.5-7.5 | – | W-3,75-5,25, V-.20-.40 | 72 | 40 | 4% |
| AC40 | Inconel 600 | ASTM-A494 | N06040 | 0.4 | 14.0-17.0 | BAL | – | – | 11 | – | – | 70 | 28 | 30% |
| CZ100 | Níquel fundido | ASTM-A494 | N02100 | 1 | – | 95,0 minutos. | – | 1.25 | 3 | – | – | 50 | 18 | 10% |
| N7M | Hastelloy B modificado | ASTM-A494 | N30007 | 0.07 | 1 | BAL | 30.0-33.0 | – | 3 | – | – | 76 | 40 | 20% |
| N12MV | Hastelloy B | ASTM-A494 | N30012 | 0.12 | 1 | BAL | 26.0-30.0 | – | 4.0-6.0 | – | – | 76 | 40 | 6% |
| M35-1 | Monel 400 | ASTM-A494, A990 | N24135 | 0.35 | – | BAL | – | 26.0-33.0 | 3.5 | 0.5 | Si 1,25 | 65 | 25 | 25% |
| M35-2 | Monel | ASTM-A494 | N04020 | 0.35 | – | BAL | – | 26.0-33.0 | 3.5 | – | Si 2.0 | 65 | 30 | 25% |
| M35-B/M30H | H-Monel | ASTM-A494, QQ-N-288 Comp B | N24030 | 0.3 | – | BAL | – | 27.0-33.0 | 2.5 | – | Si 2,7-3,9 | 700 | 60 | 10% |
| M35-C | Monel | QQ-N-288 Comp C | N24025 | 0.2 | – | BAL | – | 27.0-31.0 | 2.5 | – | Si 3,3-3,7 | 120 | 80 | 10% |
| M35-D/M25S | S-Monel | ASTM A494, QQ-N-288 Comp D | N24025 | 0.25 | – | BAL | – | 27.0-31.0 | 2.5 | – | Si 3,5-4,5 | – | – | – |
| M30C/M35W | Monel Soldável | ASTM-A494, QQ-N-288 Comp E | N24130 | 0.3 | – | BAL | – | 26.0-33.0 | 3.5 | – | Si 1,0-2,0, Cb 1,0-3,0 | 65 | 32.5 | 25% |
| 952 | Al Bronze Grau A | ASTM-B148 | C95200 | – | – | – | – | 86,0 minutos | 2.5-4.0 | – | Al 8,5-9,5 | 65 | 25 | 20% |
| 954 | Alumínio-Bronze | ASTM-B148 | C95400 | – | – | 1,5 máx. | – | 83,0 minutos | 3.0-5.0 | – | Al 10,0-11,5 | 75 | 30 | 12% |
| 955 | Alumínio-Bronze | ASTM-B148 | C95500 | – | – | 3.0-5.5 | – | 78,0 minutos | 3.0-5.0 | – | Al 10,0-11,5 | 90 | 40 | 6% |
| 958 | Ni-Al-Brz | ASTM-B148 | C95800 | – | – | 4.0-5.0 | – | 79,0 minutos | 3.0-4.5 | – | Al 8,5-9,5 Pb 0,03 máx. | 85 | 35 | 15% |
| 964 | 70*30 Cobre-Níquel | ASTM-B369 | C96400 | 0.15 | – | 28.0-32.0 | – | BAL | .25-1.5 | 0.5-1.5 | Mn 1,5 | 60 | 32 | 20% |
| CD4MCuN | Duplex Grau 1B | ASTM-A890, A995 | J93372 | 0.04 | 24.5-26.5 | 4.75-6.0 | 1.75-2.25 | 2.75-3.25 | BAL | – | N 0,10-0,25 | 100 | 70 | 16% |
| CD3MCuN | Duplex Grau 1C | ASTM-A890 | J93373 | 0.03 | 24-26.7 | 5.6-6.7 | 2.9-3.8 | 1.4-1.9 | BAL | – | N 0,22-0,33 | 100 | 65 | 25% |
| CE8MN | Duplex Grau 2A | ASTM-A351, A890, A995 | J93345 | 0.08 | 22.5-25.5 | 8.0-11.0 | 3.00-4.50 | – | BAL | – | N 0,10-0,30 | 95 | 65 | 25% |
| CD6MN | Duplex Grau 3A | ASTM-A890, A995 | J93371 | 0.06 | 24.0-27.0 | 4.0-6.0 | 1.75-2.50 | – | BAL | – | N 0,10-0,25 | 95 | 65 | 25% |
| CD3MN | Duplex Grau 4A | ASTM-A890, A995 | J92205 | 0.03 | 21.0-23.5 | 4.5-6.5 | 2.5-3.5 | 1,00 no máximo | BAL | – | N 0,10-0,30 | 90 | 60 | 25% |
| CE3MN | Duplex Grau 5A | ASTM-A890, A995 | J93404 | 0.03 | 24.0-26.0 | 6.0-8.0 | 4.0-5.0 | – | BAL | – | N 0,10-0,03 | 100 | 75 | 18% |
| CD3MWCuN | Grau 6A Zeron100 | ASTM-A890, A995 | J93380 | 0.03 | 24.0-26.0 | 6.5-8.5 | 3.0-4.0 | 0.5-1.0 | BAL | – | N 0,02-0,03 W 0,5-1,0 | 100 | 65 | 25% |
| HH | ASTM-A297 | ASTM-A297 | J93503 | 0.20-0.50 | 24.0-28.0 | 11.0-14.0 | 0.5 | 1 | BAL | – | – | 75 | 35 | 10% |
| Hong Kong | ASTM-A297 | ASTM-A297 | J94224 | 0.20-0.60 | 24.0-28.0 | 18.0-22.0 | 0.5 | 1 | BAL | – | – | 65 | 35 | 10% |
| HN | HI-35 | ASTM-A297 | J94213 | 0.20-0.50 | 19.0-23.0 | 23.0-27.0 | 0.5 | 1 | BAL | – | – | 63 | – | 8% |
| HT | 330 (15-35) | ASTM-A297 | N08605 | 0.35-0.75 | 15.0-19.0 | 33.0-37.0 | 0.5 | 1 | BAL | – | – | 65 | – | 4% |
| UH | (19-39) | ASTM-A297 | N08004 | 0.35-0.75 | 17.0-21.0 | 37.0-41.0 | 0.5 | 1 | BAL | – | – | 65 | – | 4% |
| HX | ACI HX | ASTM-A297 | N06006 | 0.35-0.75 | 15.0-19.0 | 64.0-68.0 | 0.5 | 1 | BAL | – | – | 60 | – | – |
| WCA | Aço carbono | ASTM-A216 | J02502 | 0.25 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 60-85 | 30 | 24% |
| WCB | Aço carbono | ASTM-A216 | J03002 | 0.3 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 70-95 | 36 | 22% |
| CMI | Aço carbono | ASTM-A216 | J02503 | 0.25 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 70-95 | 40 | 22% |
| LCB | Aço carbono | ASTM-A352 | J03003 | 0.3 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 65 | 35 | 24% |
| CCB | Aço carbono | ASTM-A352 | J02505 | 0.25 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 70 | 40 | 22% |
| LC2 | ASTM-A352 | J22500 | 0.25 | – | 2.00-3.00 | 0.45-0.65 | – | BAL | – | – | 70.0-95.0 | 40.0 | 24% | |
| LC3 | ASTM-A352 | J31550 | 0.15 | – | 3.00-4.00 | – | – | BAL | – | – | 70.0-95.0 | 40.0 | 24% | |
| WC6 | ASTM-A217 | J12072 | 0.05-0.20 | 1.00-1.50 | – | 0.45-0.65 | 0.50 | BAL | – | – | 70-95 | 40 | 20% | |
| WC9 | ASTM-A217 | J21890 | 0.05-0.18 | 2.00-2.75 | – | 0.90-1.20 | 0.50 | BAL | – | – | 70-95 | 40 | 20% | |
| C5 | ASTM-A217 | J42045 | 0.20 | 4.00-6.50 | – | 0.45-0.65 | 0.50 | BAL | – | – | 90-115 | 60 | 18% | |
| C12 | ASTM-A217 | J82090 | 0.20 | 8.00-10.00 | – | 0.90-1.20 | 0.50 | BAL | – | – | 90-115 | 60 | 18% | |
| C12A | 91ª série | ASTM-A217 | J84090 | 0.08-0.12 | 8.0-9.5 | 0.40 | 0.85-1.05 | – | BAL | 0.060-0.10 | N 0,030-0,070, V 0,18-0,25 | 85-110 | 60 | 18% |
| SC8625 | ASTM A487, A148 | 0.30 | 0.40-0.80 | 0.40-0.80 | 0.15-0.30 | 0.50 | BAL | – | – | 105-130 | 85 | 17% |
Hastelloy C276 (ASTM A 494, Grau CW12MW)
As válvulas Hastelloy C276 de instrumentação de alto desempenho possuem resistência superior a vários ácidos. Por exemplo, as válvulas esfera Hastelloy C276 têm a capacidade de resistir a ácidos como ácido sulfúrico, clorídrico, fluorídrico, nítrico e crômico. A Válvula Esfera Hastelloy ainda possui boa resistência à corrosão localizada.
CW12MW é a antiga liga Hastelloy C fundida original. Seu limite mais alto de carbono de 0,12% no máximo, juntamente com seus níveis mais altos de ferro e tungstênio, tornam esta liga inferior a qualquer um dos outros graus em resistência à corrosão e ductilidade. CW12MW não é o equivalente fundido para UNS N10276.
CW6M
CW6M é a próxima liga fundida de Ni-Cr-Mo desenvolvida. Foi introduzido em 1949, portanto há uma longa e bem-sucedida história para esta liga. Embora tenha um limite permitido de carbono e silício mais alto do que os tipos C mais recentes listados abaixo, normalmente é feito com níveis muito mais baixos de carbono e silício, proporcionando assim boa resistência à corrosão tanto para ácidos oxidantes quanto redutores.
CW2M
CW2M é o equivalente fundido do UNS N06455 desenvolvido em 1976 para fornecer melhor estabilidade metalúrgica do que o UNS N10276 em altas temperaturas. Um benefício adicional foi que é uma classe fundida melhor que a CW12MW. Seu melhor desempenho em relação ao CW12MW foi resultado da redução da quantidade de fases intermetálicas em sua microestrutura. Isso foi conseguido reduzindo os níveis de carbono, silício, ferro, cromo e molibdênio e eliminando a adição de tungstênio.
CX2MW
CX2MW é o equivalente fundido do UNS N06022. Esta liga possui maior teor de cromo, mas menor teor de molibdênio do que outras ligas do tipo Hastelloy C. O maior teor de cromo confere a esta liga melhor resistência à corrosão em ambientes oxidantes quentes, como alvejantes e salmouras cloradas. Contudo, o menor teor de molibdênio sacrifica alguma resistência à redução de serviços onde estas ligas também são comumente usadas, por exemplo, ácidos sulfúrico e clorídrico.
CX2M
CX2M é o equivalente fundido ao UNS N06059. Possui cromo e molibdênio ligeiramente mais elevados que o CX2MW. O maior teor de cromo pode proporcionar boa resistência a serviços oxidantes fortes e seu maior teor de molibdênio pode proporcionar boa resistência aos ácidos sulfúrico e clorídrico.
UNS N06200
UNS N06200 (Hastelloy C-2000) é a mais nova liga do tipo C, mas só está disponível como componente forjado porque seu teor extremamente baixo de carbono e silício significa que não é benéfico para fazer uma liga fundida. UNS N06200 contém um teor de cromo semelhante ao UNS N06022, mas possui mais molibdênio junto com uma pequena quantidade de cobre. O maior teor de molibdênio junto com o cobre confere à liga melhor resistência à redução de ácidos como sulfúrico e clorídrico.
Etiquetas relacionadas :
Dez artigos antes e depois
Portuguese 
English 
German 
Spanish 
French 
Russian 
Turkish