ORTAK VALF DÖKÜM MALZEMELERİ METALURJİSİ
| Dökme Alaşım | Benzer Dövme Tanımı | Şartname | UNS No. | C | CR | Ni | Ay | Cu | Fe | Cb | Diğer | Çekme (ksi) | Verim (ksi) | Uzat |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| CA6NM | 415, F6NM | ASTM-A743, A487 | J91540 | 0.06 | 11.5-14.0 | 3.5-4.5 | .4-1.0 | – | BAL | – | – | 110 | 80 | 17% |
| CA15 | 410 | ASTM-A217, A743 | J91150 | 0.15 | 11.5-14.0 | 1 | 0.5 | 0.5 | BAL | – | – | 90 | 65 | 18% |
| CB7Cu-1 | 17-4 PH | ASTM-A747, AMS-5398C | J92180 | 0.06 | 15.5-17.7 | 3.6-4.6 | – | 2.5-3.2 | BAL | .15-.35 | – | 135 H1100 Durumu | 100 | 9% |
| CF3 | 304L | ASTM-A351, A743, A744 | J92500 | 0.03 | 17.0-21.0 | 8.0-12.0 | 0.5 | – | BAL | – | – | 70 | 30 | 35% |
| CF3MN | 316LN | ASTM-A743, A351 | J92804 | 0.03 | 17.0-21.0 | 9.0-13.0 | 2.0-3.0 | – | BAL | – | N-0.10-0.20 | 75 | 37 | 35% |
| CF3M | 316L | ASTM-A351, A743, A744 | J92800 | 0.03 | 17.0-21.0 | 9.0-13.0 | 2.0-3.0 | – | BAL | – | – | 70 | 30 | 30% |
| CF8 | 304 | ASTM-A351, A743, A744 | J92600 | 0.08 | 18.0-21.0 | 8.0-11.0 | 0.5 | – | BAL | – | – | 70 | 30 | 35% |
| CF8C | 347 | ASTM-A351, A743, A744 | J92710 | 0.08 | 18.0-21.0 | 9.0-12.0 | 0.5 | – | BAL | 8xC-1.0 | – | 70 | 30 | 30% |
| CF8M | 316 | ASTM-A351, A743, A744 | J92900 | 0.08 | 18.0-21.0 | 9.0-12.0 | 2.0-3.0 | – | BAL | – | – | 70 | 30 | 30% |
| CG3M | 317L | ASTM-A351, A743, A744 | J92999 | 0.03 | 18.0-21.0 | 9.0-13.0 | 3.0-4.0 | – | BAL | – | – | 75 | 35 | 25% |
| CG8M | 317 | ASTM-A351, A743, A744 | J93000 | 0.08 | 18.0-21.0 | 9.0-13.0 | 3.0-4.0 | – | BAL | – | – | 75 | 35 | 25% |
| CN7M | Alaşım 20 | ASTM-A351, A743, A744 | N08007 | 0.07 | 19.0-22.0 | 27.5-30.5 | 2.0-3.0 | 3.0-4.0 | BAL | – | – | 62 | 25 | 35% |
| CN2MCuN | 904L | N08904 | 0.02 | 19.0-23.0 | 23.0-28.0 | 4.0-5.0 | 1.0-2.0 | BAL | – | – | 65 | 28 | 35% | |
| CK3MCuN | Avesta 254-SMO | ASTM-A351, A743, A744 | J93254 | 0.025 | 19.5-20.5 | 17.5-19.5 | 6.00-7.00 | 0.50-1.00 | BAL | – | N 0,18-0,24 | 80 | 38 | 35% |
| CN3MN | AL6XN | ASTM-A351, A743, A744 | J94651 | 0.030 | 20.0-22.0 | 23.5-25.5 | 6.0-7.0 | 0.75 | BAL | – | N 0,18-1,26 | 80 | 38 | 35% |
| CX2MW | Hastelloy C-22 | ASTM A494 | N26022 | 0.02 | 20.0-22.5 | BAL | 12.5-14.5 | – | 2.0-6.0 | – | W-2.5-3.5 | 80 | 45 | 30% |
| CW2M | Hastelloy C4C | ASTM-A494, A990 | N26455 | 0.02 | 15.0-17.5 | BAL | 15.0-17.5 | – | 2 | – | – | 72 | 40 | 20% |
| CW6M | Hastelloy C Modifiye | ASTM-A494 | N30107 | 0.07 | 17.0-20.0 | BAL | 17.0-20.0 | – | 3 | – | – | 72 | 40 | 25% |
| CW6MC | İnkonel 625 | ASTM-A494, MIL-C-24615 | N26625 | 0.06 | 20.0-23.0 | BAL | 8.0-10.0 | – | 5 | 3.15-4.5 | – | 70 | 40 | 25% |
| CW12MW | Hastelloy C | ASTM-A494 | N30002 | 0.12 | 15.5-17.5 | BAL | 16.0-18.0 | – | 4.5-7.5 | – | G-3.75-5.25, V-.20-.40 | 72 | 40 | 4% |
| CW12MW | Hastelloy C-276 | ASTM-A494 | N30002 | 0.02 | 15.5-17.5 | BAL | 16.0-18.0 | – | 4.5-7.5 | – | G-3.75-5.25, V-.20-.40 | 72 | 40 | 4% |
| CY40 | İnkonel 600 | ASTM-A494 | N06040 | 0.4 | 14.0-17.0 | BAL | – | – | 11 | – | – | 70 | 28 | 30% |
| CZ100 | Dökme Nikel | ASTM-A494 | N02100 | 1 | – | 95.0 dk. | – | 1.25 | 3 | – | – | 50 | 18 | 10% |
| N7M | Hastelloy B Modifiye | ASTM-A494 | N30007 | 0.07 | 1 | BAL | 30.0-33.0 | – | 3 | – | – | 76 | 40 | 20% |
| N12MV | Hastelloy B | ASTM-A494 | N30012 | 0.12 | 1 | BAL | 26.0-30.0 | – | 4.0-6.0 | – | – | 76 | 40 | 6% |
| M35-1 | Monel 400 | ASTM-A494, A990 | N24135 | 0.35 | – | BAL | – | 26.0-33.0 | 3.5 | 0.5 | Si 1,25 | 65 | 25 | 25% |
| M35-2 | Monel | ASTM-A494 | N04020 | 0.35 | – | BAL | – | 26.0-33.0 | 3.5 | – | Si 2.0 | 65 | 30 | 25% |
| M35-B / M30H | H-Monel | ASTM-A494, QQ-N-288 Komp B | N24030 | 0.3 | – | BAL | – | 27.0-33.0 | 2.5 | – | Si 2,7-3,9 | 700 | 60 | 10% |
| M35-C | Monel | QQ-N-288 Comp C | N24025 | 0.2 | – | BAL | – | 27.0-31.0 | 2.5 | – | Si 3.3-3.7 | 120 | 80 | 10% |
| M35-D / M25S | S-Monel | ASTM A494, QQ-N-288 Comp D | N24025 | 0.25 | – | BAL | – | 27.0-31.0 | 2.5 | – | Si 3,5-4,5 | – | – | – |
| M30C / M35W | Kaynaklanabilir Monel | ASTM-A494, QQ-N-288 Zorunlu E | N24130 | 0.3 | – | BAL | – | 26.0-33.0 | 3.5 | – | Si 1,0-2,0, Cb 1,0-3,0 | 65 | 32.5 | 25% |
| 952 | Al Bronz Sınıf A | ASTM-B148 | C95200 | – | – | – | – | 86.0 dakika | 2.5-4.0 | – | Al 8.5-9.5 | 65 | 25 | 20% |
| 954 | Alüminyum-Bronz | ASTM-B148 | C95400 | – | – | maksimum 1,5 | – | 83.0 dakika | 3.0-5.0 | – | Al 10.0-11.5 | 75 | 30 | 12% |
| 955 | Alüminyum-Bronz | ASTM-B148 | C95500 | – | – | 3.0-5.5 | – | 78.0 dakika | 3.0-5.0 | – | Al 10.0-11.5 | 90 | 40 | 6% |
| 958 | Ni-Al-Brz | ASTM-B148 | C95800 | – | – | 4.0-5.0 | – | 79,0 dk | 3.0-4.5 | – | Al 8,5-9,5 Pb 0,03 maks | 85 | 35 | 15% |
| 964 | 70*30 Bakır-Nikel | ASTM-B369 | C96400 | 0.15 | – | 28.0-32.0 | – | BAL | .25-1.5 | 0.5-1.5 | Min 1,5 | 60 | 32 | 20% |
| CD4MCuN | Dubleks Sınıf 1B | ASTM-A890, A995 | J93372 | 0.04 | 24.5-26.5 | 4.75-6.0 | 1.75-2.25 | 2.75-3.25 | BAL | – | N 0,10-0,25 | 100 | 70 | 16% |
| CD3MCuN | Dubleks Sınıf 1C | ASTM-A890 | J93373 | 0.03 | 24-26.7 | 5.6-6.7 | 2.9-3.8 | 1.4-1.9 | BAL | – | N 0,22-0,33 | 100 | 65 | 25% |
| CE8MN | Dubleks Sınıf 2A | ASTM-A351, A890, A995 | J93345 | 0.08 | 22.5-25.5 | 8.0-11.0 | 3.00-4.50 | – | BAL | – | N 0,10-0,30 | 95 | 65 | 25% |
| CD6MN | Dubleks Sınıf 3A | ASTM-A890, A995 | J93371 | 0.06 | 24.0-27.0 | 4.0-6.0 | 1.75-2.50 | – | BAL | – | N 0,10-0,25 | 95 | 65 | 25% |
| CD3MN | Dubleks Sınıf 4A | ASTM-A890, A995 | J92205 | 0.03 | 21.0-23.5 | 4.5-6.5 | 2.5-3.5 | Maksimum 1,00 | BAL | – | N 0,10-0,30 | 90 | 60 | 25% |
| CE3MN | Dubleks Sınıf 5A | ASTM-A890, A995 | J93404 | 0.03 | 24.0-26.0 | 6.0-8.0 | 4.0-5.0 | – | BAL | – | N 0,10-0,03 | 100 | 75 | 18% |
| CD3MWCuN | Sınıf 6A Zeron100 | ASTM-A890, A995 | J93380 | 0.03 | 24.0-26.0 | 6.5-8.5 | 3.0-4.0 | 0.5-1.0 | BAL | – | K 0,02-0,03 W 0,5-1,0 | 100 | 65 | 25% |
| HH | ASTM-A297 | ASTM-A297 | J93503 | 0.20-0.50 | 24.0-28.0 | 11.0-14.0 | 0.5 | 1 | BAL | – | – | 75 | 35 | 10% |
| Hong Kong | ASTM-A297 | ASTM-A297 | J94224 | 0.20-0.60 | 24.0-28.0 | 18.0-22.0 | 0.5 | 1 | BAL | – | – | 65 | 35 | 10% |
| HN | HI-35 | ASTM-A297 | J94213 | 0.20-0.50 | 19.0-23.0 | 23.0-27.0 | 0.5 | 1 | BAL | – | – | 63 | – | 8% |
| HT | 330 (15-35) | ASTM-A297 | N08605 | 0.35-0.75 | 15.0-19.0 | 33.0-37.0 | 0.5 | 1 | BAL | – | – | 65 | – | 4% |
| HÜ | (19-39) | ASTM-A297 | N08004 | 0.35-0.75 | 17.0-21.0 | 37.0-41.0 | 0.5 | 1 | BAL | – | – | 65 | – | 4% |
| HX | ACI HX | ASTM-A297 | N06006 | 0.35-0.75 | 15.0-19.0 | 64.0-68.0 | 0.5 | 1 | BAL | – | – | 60 | – | – |
| WCA | Karbon çelik | ASTM-A216 | J02502 | 0.25 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 60-85 | 30 | 24% |
| WCB | Karbon çelik | ASTM-A216 | J03002 | 0.3 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 70-95 | 36 | 22% |
| WCC | Karbon çelik | ASTM-A216 | J02503 | 0.25 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 70-95 | 40 | 22% |
| LCB | Karbon çelik | ASTM-A352 | J03003 | 0.3 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 65 | 35 | 24% |
| düşük maliyetli | Karbon çelik | ASTM-A352 | J02505 | 0.25 | 0.5 | 0.5 | 0.2 | 0.3 | BAL | – | – | 70 | 40 | 22% |
| LC2 | ASTM-A352 | J22500 | 0.25 | – | 2.00-3.00 | 0.45-0.65 | – | BAL | – | – | 70.0-95.0 | 40.0 | 24% | |
| LC3 | ASTM-A352 | J31550 | 0.15 | – | 3.00-4.00 | – | – | BAL | – | – | 70.0-95.0 | 40.0 | 24% | |
| WC6 | ASTM-A217 | J12072 | 0.05-0.20 | 1.00-1.50 | – | 0.45-0.65 | 0.50 | BAL | – | – | 70-95 | 40 | 20% | |
| WC9 | ASTM-A217 | J21890 | 0.05-0.18 | 2.00-2.75 | – | 0.90-1.20 | 0.50 | BAL | – | – | 70-95 | 40 | 20% | |
| C5 | ASTM-A217 | J42045 | 0.20 | 4.00-6.50 | – | 0.45-0.65 | 0.50 | BAL | – | – | 90-115 | 60 | 18% | |
| C12 | ASTM-A217 | J82090 | 0.20 | 8.00-10.00 | – | 0.90-1.20 | 0.50 | BAL | – | – | 90-115 | 60 | 18% | |
| C12A | 91. Sınıf | ASTM-A217 | J84090 | 0.08-0.12 | 8.0-9.5 | 0.40 | 0.85-1.05 | – | BAL | 0.060-0.10 | N 0,030-0,070, V 0,18-0,25 | 85-110 | 60 | 18% |
| SC8625 | ASTM A487, A148 | 0.30 | 0.40-0.80 | 0.40-0.80 | 0.15-0.30 | 0.50 | BAL | – | – | 105-130 | 85 | 17% |
Hastelloy C276 (ASTM A 494, Sınıf CW12MW)
Yüksek performanslı Enstrümantasyon Hastelloy C276 Valfleri çeşitli asitlere karşı üstün dirence sahiptir. Örneğin Hastelloy C276 Küresel Vanalar sülfürik, hidroklorik, hidroflorik, nitrik ve kromik asit gibi asitlere karşı direnç gösterme özelliğine sahiptir. Hastelloy Küresel Vana, lokal korozyona karşı da iyi bir dirence sahiptir.
CW12MW eski orijinal döküm Hastelloy C alaşımıdır. Maksimum 0,12%'lik daha yüksek karbon limiti ve daha yüksek demir ve tungsten seviyeleri, bu alaşımı korozyon direnci ve süneklik açısından diğer kalitelerden daha aşağı hale getirir. CW12MW, UNS N10276'nın döküm eşdeğeri değildir.
CW6M
CW6M geliştirilen bir sonraki döküm Ni-Cr-Mo alaşımıdır. 1949 yılında piyasaya sürüldüğü için bu alaşımın uzun ve başarılı bir geçmişi vardır. Aşağıda listelenen yeni C türlerinden daha yüksek izin verilen karbon ve silikon sınırına sahip olmasına rağmen, genellikle çok daha düşük karbon ve silikon seviyelerinden yapılır, böylece hem oksitleyici hem de indirgeyici asitlere karşı iyi bir korozyon direnci sağlar.
CW2M
CW2M, yüksek sıcaklıklarda UNS N10276'ya göre daha iyi metalurjik stabilite sağlamak üzere 1976'da geliştirilen UNS N06455'in döküm eşdeğeridir. Ek bir faydası da CW12MW'den daha iyi bir döküm kalitesi olmasıydı. CW12MW'ye göre geliştirilmiş performansı, mikro yapısında metaller arası fazların miktarının azalmasının bir sonucuydu. Bu, karbon, silikon, demir, krom ve molibden seviyelerinin düşürülmesi ve tungsten ilavesinin ortadan kaldırılmasıyla gerçekleştirildi.
CX2MW
CX2MW, UNS N06022'nin döküm eşdeğeridir. Bu alaşım diğer Hastelloy C tipi alaşımlara göre daha yüksek krom içeriğine sahiptir ancak molibden içeriği daha düşüktür. Daha yüksek krom içeriği, bu alaşıma ağartıcı ve klorlu tuzlu su gibi sıcak oksitleyici ortamlara karşı daha iyi korozyon direnci sağlar. Bununla birlikte, daha düşük molibden içeriği, bu alaşımların da yaygın olarak kullanıldığı durumlarda, örneğin sülfürik ve hidroklorik asitler gibi indirgeyici hizmetlere karşı direncin bir kısmını feda eder.
CX2M
CX2M, UNS N06059'un döküm eşdeğeridir. CX2MW'den biraz daha yüksek krom ve molibden içerir. Daha yüksek krom, güçlü oksitleyici hizmetlere karşı iyi bir direnç sağlayabilir ve daha yüksek molibden içeriği, sülfürik ve hidroklorik asitlere karşı iyi bir direnç sağlayabilir.
UNS N06200
UNS N06200 (Hastelloy C-2000) en yeni C tipi alaşımdır, ancak yalnızca işlenmiş bir bileşen olarak mevcuttur çünkü son derece düşük karbon ve silikon içeriği, döküm alaşımı yapımında faydalı olmadığı anlamına gelir. UNS N06200, UNS N06022'ye benzer bir krom içeriği içerir, ancak az miktarda bakırın yanı sıra daha fazla molibden içerir. Bakırla birlikte daha yüksek molibden içeriği, alaşıma sülfürik ve hidroklorik gibi indirgeyici asitlere karşı daha iyi direnç kazandırır.
İlgili Etiketler :
Öncesi ve sonrasıyla on makale
Turkish 
English 
German 
Spanish 
French 
Russian 
Portuguese